     德州市鑫华润科技股份有限公司A/B料产品说明书
    De Zhou Xin HuaRun Technology CO., LTD.
  A/B Shoe Materials Product Manuals

1.特点(Feature :坡跟鞋底用料(Polyester polyol for wedges soles
2.原液特性: Typical properties of PU resin:


品名
Name of products

外观
Appearance
(40)

粘度
Viscosity
(mPa´s/40)

密度
Density
(g/cm³/40)

包装
Package
(kg)

保质期
Shelf life
(month)

贮存温度
Storage temperature
()

HR-P-1207

液状
Liquid

2000±200

1.2±0.02

18 (Net)
蓝标签
Blue label

6

20~25

HR-I-2206

液状或蜡状Liquid or waxy

200±50

1.20±0.02

20 (Net)
黄标签
Yellow label

3

20~25

3.催化剂与辅助剂Catalyst & Additives:
催化剂HR-C-3的加入量为:250±10g/18kg,水的加入量为:90-110g/18kg
The adding amount of HR-C-3 should be 250±10g/18kg, the adding amount of water should be 90-110g/18kg.
4.成型条件及物性值:Typical processing parameters & Typical Properties:


反应性
Reaction
characteristics

技术参数
Technical
parameters

项目
Items

物性值
Physical
properties

参考配比
A+C/B Mix ratio (By Weight)

100/85-90

成型密度(g/m3)
Molded density (g/m3)

0.45-0.55

使用温度(℃)
Material Temperature (℃)

38-42/38-42

硬度
Hardness

A型Asker A

65-80

C型Asker C

 

乳白时间(s)
Cream time (s)

4-6

拉伸强度(MPa)
Tensile strength (MPa)

≥5.0

升起时间(s)
Rise time (s)

30-35

伸长率(%)
Elongation (%)

≥400

自由泡密度(g/m³)
Free rise foam density (g/m³)

0.23-0.25

撕裂强度(直角)(kN/m)
Tear strength (right angle) (kN/m)

≥8.0

金属模具温度(℃)
Mold temperature (℃)

45-55

耐折性(常温25℃×10万次)
Folding endurance (25℃×10 million times)

无裂纹

脱模时间(min)
Demould time (min)

4-6

DIN耐磨
DIN abrasion resistance

≤200

  • 配合比率是以最佳配比值为基础,此配比值会随添加的颜料助剂种类和添加量不同而变化。The mixing ratio is based on the best proportion, this ratio will be changed with the kind of dye and its adding amount.
  • 自由泡沫密度会依季节(温度,湿度)的不同而变化。Free rise density may vary with temperature & humidity.
  • 该物性数据是对6mm厚的试验片测试获得的数据。These physical data are acquired by testing a sample of 6mm thick.
  • 以上数据仅供参考,具体数据以实际操作为准,如需其他物性指标,请与我公司联系。Data listed above are just for reference.  The detail data are subject to practice operation. If other physical properties are required, please contact us.